Water Absorption at Saturation飽和水吸收率
|
0.20 %
@Temperature 23.0 °C
|
0.20 %
@Temperature 73.4 °F
|
ISO 62
|
Linear Mold Shrinkage, Flow線性收縮率/流動
|
0.0040 - 0.0060 cm/cm
@Thickness 3.20 mm
|
0.0040 - 0.0060 in/in
@Thickness 0.126 in
|
SABIC Method
|
Melt Flow熔體流動速率
|
15 g/10 min
@Load 2.16 kg,
Temperature 260 °C
|
15 g/10 min
@Load 4.76 lb,
Temperature 500 °F
|
[cm^3/10 min] Melt Volume Rate; ISO 1133
|
|
18 g/10 min
@Load 2.16 kg,
Temperature 260 °C
|
18 g/10 min
@Load 4.76 lb,
Temperature 500 °F
|
ASTM D 1238
|